Nitto Denko – Hà Sơn https://congcusanxuat.vn Công cụ sản xuất Thu, 04 Apr 2024 06:08:06 +0000 vi hourly 1 https://wordpress.org/?v=6.5.8 https://congcusanxuat.vn/wp-content/uploads/2020/03/cropped-logo2-2-32x32.gif Nitto Denko – Hà Sơn https://congcusanxuat.vn 32 32 Băng keo trắng NITTO 2107TV 19mm https://congcusanxuat.vn/san-pham/bang-keo-trang-nitto-2107tv-19mm/ Mon, 01 Apr 2024 07:23:29 +0000 https://congcusanxuat.vn/?post_type=product&p=16604 Băng keo trắng NITTO 2107TV 19mm]]>
Thickness [mm] Width [mm] Length [m] Color
0.13 10,19,25,30 20 Black,White,Green,Yellow,Gray,Blue,Red,Pink,Orange,
Brown,Purple,Sky Blue,Light Green,Transparent

*For other sizes, please contact us.

Property Unit No.2107TV
Thickness [mm] 0.119
Adhesive strength (to stainless steel plate) [N/19mm] 2.38
Tensile strength 39.2
Elongation [%] 199
]]> Băng keo trắng NITTO 2107TV 10mm https://congcusanxuat.vn/san-pham/bang-keo-trang-nitto-2107tv-10mm/ Mon, 01 Apr 2024 07:22:20 +0000 https://congcusanxuat.vn/?post_type=product&p=16603 Băng keo trắng NITTO 2107TV 10mm]]>
Thickness [mm] Width [mm] Length [m] Color
0.13 10,19,25,30 20 Black,White,Green,Yellow,Gray,Blue,Red,Pink,Orange,
Brown,Purple,Sky Blue,Light Green,Transparent

*For other sizes, please contact us.

Property Unit No.2107TV
Thickness [mm] 0.119
Adhesive strength (to stainless steel plate) [N/19mm] 2.38
Tensile strength 39.2
Elongation [%] 199
]]> Băng keo NITTO No.903UL (0.08mm x 250mm x 10m) https://congcusanxuat.vn/san-pham/bang-keo-nitto-no-903ul-0-08mm-x-250mm-x-10m/ Mon, 01 Apr 2024 07:19:59 +0000 https://congcusanxuat.vn/?post_type=product&p=16602 Băng keo NITTO No.903UL (0.08mm x 250mm x 10m)]]> Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,100,200,250,300,350,400,450 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]> Băng keo Gray NITTO 2107TV https://congcusanxuat.vn/san-pham/bang-keo-gray-nitto-2107tv/ Mon, 01 Apr 2024 07:18:28 +0000 https://congcusanxuat.vn/?post_type=product&p=16600 Băng keo Gray NITTO 2107TV]]>

Specifications

Thickness [mm] Width [mm] Length [m] Color
0.13 10,19,25,30 20 Black,White,Green,Yellow,Gray,Blue,Red,Pink,Orange,
Brown,Purple,Sky Blue,Light Green,Transparent

*For other sizes, please contact us.

Properties

Property Unit No.2107TV
Thickness [mm] 0.119
Adhesive strength (to stainless steel plate) [N/19mm] 2.38
Tensile strength 39.2
Elongation [%] 199
]]> Băng keo đen NITTO 2101TV https://congcusanxuat.vn/san-pham/bang-keo-den-nitto-2101tv/ Mon, 01 Apr 2024 07:16:32 +0000 https://congcusanxuat.vn/?post_type=product&p=16598 Băng keo đen NITTO 2101TV]]> Thông số kỹ thuật

Độ dày [mm] Chiều rộng [mm] Chiều dài [m] màu
0.1 19,25,30 25 đen

* Kích thước khác xin vui lòng liên hệ với chúng tôi.

Đặc tính

đặc tính đơn vị No.2101TV
Độ dày [Mm] 0.10
Độ kết dính (tấm thép không gỉ) [N / 19mm] 2.40
Sứcbền kéo 33.3
Sự giãn dài [%] 187
]]> Băng keo chống trầy NITTO No.903UL (0.13mmx250mmx10m) https://congcusanxuat.vn/san-pham/bang-keo-chong-tray-nitto-no-903ul-0-13mmx250mmx10m/ Mon, 01 Apr 2024 07:15:04 +0000 https://congcusanxuat.vn/?post_type=product&p=16597 Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,100,200,250,300,350,400,450 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]> Băng keo chống trầy NITTO No.903UL (0.08mmx19mmx10m) https://congcusanxuat.vn/san-pham/bang-keo-chong-tray-nitto-no-903ul-0-08mmx19mmx10m/ Mon, 01 Apr 2024 07:14:17 +0000 https://congcusanxuat.vn/?post_type=product&p=16596 Băng keo chống trầy NITTO No.903UL (0.08mmx19mmx10m)]]> Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,100,200,250,300,350,400,450 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]> Băng keo chống trầy NITTO NO.903UL (0.08mmx150mmx10m) https://congcusanxuat.vn/san-pham/bang-keo-chong-tray-nitto-no-903ul-0-08mmx150mmx10m/ Mon, 01 Apr 2024 07:13:34 +0000 https://congcusanxuat.vn/?post_type=product&p=16595 Băng keo chống trầy NITTO NO.903UL (0.08mmx150mmx10m)]]> Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,100,200,250,300,350,400,450 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]> Băng keo chống trầy NITTO NO.903UL (0.08mmx100mmx10m) https://congcusanxuat.vn/san-pham/bang-keo-chong-tray-nitto-no-903ul-0-08mmx100mmx10m/ Mon, 01 Apr 2024 07:12:31 +0000 https://congcusanxuat.vn/?post_type=product&p=16594 Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,100,200,250,300,350,400,450 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]> Băng keo chống trầy NITTO No. 903UL 0.08mm*200mm*10m https://congcusanxuat.vn/san-pham/nitoflon-no-903ul/ Thu, 28 Mar 2024 09:13:29 +0000 https://congcusanxuat.vn/?post_type=product&p=16426 Standard Products Size

 

Table. 1

Thickness(mm) Width(mm) Length(m)
0.08 5,9,10,13,15,19,20,22,25,30,38,40,50,75,

100,200,250,300,350,400,450

 10
0.13
0.18
0.23

*Contact us for information concerning sizes other than standard sizes.

General Properties

 

Table. 2

Properties Unit Typical Values
0.08t 0.13t 0.18t 0.23t
Thickness mm 0.08 0.13 0.18 0.23
Tensile strength N/19mm 55 93 160 210
Elongation % 180 220 220 220
Peeling strength N/19mm 5.6 7.1 7.4 8.7
Unwinding force N/19mm 4.4 5.8 7.1 8.9
Breakdown voltage KV 8 11 14 15
Surface resistivity Ω/□ 1016
Volume resistivity Ω･cm 1015
Copper corrosion – None
Heat resistance – Good
Coefficient kinetic friction – 0.1
Flame Retardant – UL5 10 Flame Retardant (File E34833)
Color – Gray
Temperature Use Range ℃ -60 to 200

Table. 3

Name of chemicals Condition Chemical resistance1),2)
20%Sulfuric acid 80℃×24hours +++
Concentrated sulfuric acid 20℃×6days   –
Concentrated hydrochloric acid 20℃×27days +++
Concentrated hydrochloric acid 80℃×14hours +++
Concentrated nitric acid solution 20℃×25days +++
Glacial acetic acid 15℃×24hours +
20% Sodium hydroxide (NaOH) 80℃×24hours   –
20% Sodium hydroxide (NaOH) 20℃×17days ++
Ammonia water 20℃×25days +++
Toluene 80℃×14hours   –
Butanol 20℃×15days ++
Acetone 20℃×15days +++
Transformer oil 80℃×24hours +++
Machine oil 20℃×15days +++
  • +++ : No change ++ : Break away at the edge  + : Break away at same part  -: Break away completely
  • Adherent: Stainless steel (SUS304) Pressure bonding weight: 2Kg

Sample is dipped into chemical and judged by appearance of tape(NITOFLON)

]]>